Method of making thin-film magnetic head Number:7,057,260 from the United States Patent and Trademark Office (PTO) owispatent In the method of making a thin-film magnetic head in accordance with the present invention, an alignment mark is electrically connected to a multilayer film which will later become a TMR film. Therefore, when the alignment mark is irradiated with a position correcting electron beam in order to correct a drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. As a consequence, the position correcting electron beam does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.<H magnetic, making, Method, of, makin, 7057260.html, Patent, pto, 7057260

Title: Method of making thin-film magnetic head

Abstract: In the method of making a thin-film magnetic head in accordance with the present invention, an alignment mark is electrically connected to a multilayer film which will later become a TMR film. Therefore, when the alignment mark is irradiated with a position correcting electron beam in order to correct a drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. As a consequence, the position correcting electron beam does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.

Patent Number: 7,057,260 Issued on 06/06/2006 to Kagotani, legal representative, et al.

Inventors: Kagotani, legal representative; Teruyo (Saku, JP); Kasahara; Noriaki (Chuo-ku, JP); Hatake; Hitoshi (Chuo-ku, JP); Kagotani, deceased; Tsuneo (Chuo-ku, JP)
Assignee: TDK Corporation (Tokyo, JP)

Appl. No.: 379588

Filed: March 6, 2003

Foreign Application Priority Data


Mar 27, 2002 [JP]			2002-089468

Current U.S. Class: 257/620 ; 257/295; 257/296; 257/421; 257/422; 360/313; 360/314; 360/317; 428/185; 428/209; 428/469

Current International Class: H01L 23/544 (20060101); B32B 15/00 (20060101); G11B 5/127 (20060101)

References Cited [Referenced By]

U.S. Patent Documents


6534159	March 2003	Newman et al.
6886239	May 2005	Kasahara et al.

Primary Examiner: Nelms; David
Assistant Examiner: Tran; Long
Attorney, Agent or Firm: Oliff & Berridge, PLC

Claims

What is claimed is:

1. A magnetoresistive device assembly equipped with a plurality of magnetoresistive devices each having a magnetoresistive film, said magnetoresistive device assembly comprising: a substrate having an electrically insulating surface; said magnetoresistive film formed on said substrate; an alignment mark formed on said substrate, a position of said alignment mark being corrected with an electron beam; and an electrically conductive layer electrically connected to said alignment mark; wherein said electrically conductive layer and said magnetoresistive film are obtained from the same electrically conductive multilayer film.

2. A magnetoresistive device assembly equipped with a plurality of magnetoresistive devices each having a magnetoresistive film, said magnetoresistive device assembly comprising: a substrate having an electrically insulating surface; said magnetoresistive film formed on said substrate; an alignment mark formed on said substrate, a position of said alignment mark being corrected with an electron beam; and an electrically conductive layer electrically connected to said alignment mark; wherein said electrically conductive layer and said magnetoresistive film have the same laminate pattern.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method of making a thin-film magnetic head using a magnetoresistive device, a method of making a magnetoresistive device assembly, a method of making a head gimbal assembly, a method of making a hard disk drive, and a magnetoresistive device assembly.

2. Related Background Art

In recent years, as the areal density in hard disk drive (HDD) improves, thin-filmmagnetic heads playing an important role in recording and reproducing magnetic information have been required to improve their performances. As a thin-film magnetic head, a combination thin-filmmagnetic head in which a reproducing head having a magnetoresistive (MR) device and a recording head having an induction type magnetoresistive device are stacked together has recently become mainstream in place of those using an induction type magnetoresistive device for both recording and reproducing. Known as MR devices are AMR (Anisotropy Magneto Resistive) devices utilizing anisotropic magnetoresistive effect, GMR (Giant Magneto Resistive) devices utilizing giant magnetoresistive effect, TMR (Tunnel-type Magneto Resistive) devices, etc.

An example of requirements for reproducing heads is to make MR films have a very narrow track width in order to improve their reading performance. A narrow track width in MR films makes it possible to reproduce magnetic information in a hard disk having a high areal density. To respond to such a requirement, high-precision fine processing must be realized. Therefore, attempts have been made to utilize electron beam lithography capable of drawing with a precision higher than that in photolithography which had often been used in the making of thin-film magnetic heads. Electron beam lithography can make fine pattern forms, since it utilizes electron beams having a wavelength shorter than that of light.

SUMMARY OF THE INVENTION

However, the above-mentioned conventional manufacturing technique utilizing electron beam lithography has been problematic as explained in the following. For example, when patterning a TMR film on a substrate, the TMR film is coated with an electron beam resist and then is irradiated with an electron beam so as to form a desirable resist pattern, whereas drawing positions are corrected before the electron beam irradiation. For correcting the drawing positions, an alignment mark formed at an appropriate position of the substrate is initially scanned with a position correcting electron beam, and the intensity of reflected electrons occurring at this time is measured. After the position of alignment mark is detected according to the intensity of reflected electrons, the position of an optical system for emitting the drawing electron beam or the position of a stage for supporting the substrate is corrected according to the detected alignment mark position.

However, there has conventionally occurred a state where the drawing position cannot be corrected accurately, whereby the drawing electron beam cannot be emitted as aimed. In this case, the above-mentioned example fails to form the resist layer into a desirable pattern, thus making it difficult to narrow the track width of MR films such as TMR films. If the irradiation position of drawing electron beam is not accurate, reproducing track positions may shift or overlap with patterns formed in other layers, whereby the thin-film magnetic head may fail to function.

Such a problem concerning the correction of drawing positions may occur not only in the process of making TMR devices, but also in manufacturing processes utilizing electron beam lithography, i.e., processes requiring superfine processing. An example of such manufacturing processes is a step of making the upper magnetic pole of a recording head equipped with an induction type magnetoresistive device. Since the upper magnetic pole acts as an element defining the recording width of MR heads, it is necessary for the upper magnetic pole to have a narrow width in order to increase the track density. Another example of processes employing electron beam lithography is the making of a process monitoring device known as RLG (Resistance Lapping Guide) disposed in parallel with an MR device in order to adjust the MR height.

Namely, objects must be irradiated with electron beams after the drawing positions are accurately corrected in the making of the upper magnetic pole and the process monitoring device for adjusting the MR height as well.

For overcoming the problems mentioned above, it is an object of the present invention to provide a method of making a thin-film magnetic head which can accurately correct drawing positions in electron beam lithography, a method of making a magnetoresistive device assembly, a method of making a head gimbal assembly, a method of making a hard disk drive, and a magnetoresistive device assembly.

For achieving the above-mentioned object, the inventors sought after a reason why electron beam drawing positions cannot be corrected accurately. The following reason has been found as a result. First, a method of making a thin-film magnetic head will be explained in brief. Usually, a plurality of thin-film magnetic heads are made from a single wafer-like substrate. As schematically shown in FIG. 26, such a substrate typically comprises a support 101 made of AlTiC (Al.sub.2O.sub.3.TiC), for example, having a surface formed with an undercoat layer 102 made of an insulating material such as alumina (Al.sub.2O.sub.3), for example.

Laminated on the undercoat layer 102 is a lower shield layer 103 made of Permalloy (NiFe), for example, for blocking unnecessary external magnetic fields. The lower shield layer 103 is formed with an appropriate gap from its neighboring lower shield layer 103. Further laminated on each shield layer 103 is a nonmagnetic, electrically conductive lower gap layer 104 made of NiCr, Au, Ta, Cu, Al, or the like, for example.

Subsequently, the forming of a TMR film 110 on each lower gap layer 104 begins. Though not depicted, the TMR film 110 has a laminate structure comprising a free layer made of Fe, Co, Ni, or the like; a tunnel barrier layer, made of Al.sub.2O.sub.3 or the like, transmitting a tunnel current therethrough; a pinned layer yielding a constant magnetization direction regardless of external magnetic fields; and a pinning layer for fixing the magnetization direction of the pinned layer. Preferably, a cap layer made of Ta, NiCr, or the like, for example, for preventing the TMR film from oxidizing is formed on the pinning layer. Then, thus laminated TMR film 110 is subjected to electron beam lithography so as to define a narrow track width on the lower gap layer 104.

FIG. 26 is a schematic view showing the process of subjecting the TMR film 110 to electron beam lithography. When starting the electron beam lithography, the TMR film 110 is initially etched so as to form an alignment mark 105. Thereafter, the whole surface of the substrate is coated with an electron beam resist 111. Used here is a negative type resist whose part irradiated with a drawing electron beam becomes hard to dissolve in a developing solution and thus will remain as a resist layer. Subsequently, the alignment mark 105 is irradiated with a position correcting electron beam, and the electron beam irradiation position is corrected for the subsequent step of patterning the TMR film 110.

At thus corrected irradiation position, the electron beam resist 111 is irradiated with a drawing electron beam, and is subjected to postbaking, developing, and so forth, so as to form a resist layer with a desirable pattern on the lower gap layer 104. Then, ion milling or the like utilizing the resist layer as a mask etches the TMR film 110 into a desirable pattern.

However, the inventors have found that, when scanning the alignment mark 105 with the position correcting electron beam, electric charges of the emitted electron beam are stored in the alignment mark 105 as schematically shown in FIG. 26. Namely, since the undercoat layer 102 formed from an insulating material exists under the TMR film 110, the electric charges stored in the TMR film 110 cannot escape to the outside, thereby causing so-called "charge-up".

When irradiating the alignment mark 105 with electron beams, such charge-up inhibits negatively charged electron beams from advancing straightforward due to a repulsive force as indicated by arrows in FIG. 26, which lowers the accuracy in measuring the position of alignment mark 105, thus failing to attain an accurate correction factor for the drawing electron beam irradiation position.

Under such a background, the inventors have accomplished the present invention as follows:

The present invention provides a method of making a thin-film magnetic head equipped with a magnetoresistive device having a magnetoresistive film, the method comprising the steps of forming a multilayer film to become the magnetoresistive film on a substrate having an electrically insulating surface; forming an alignment mark, electrically connected to the multilayer film, for correcting a drawing position of a drawing electron beam; coating the multilayer film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; and forming the multilayer film into the magnetoresistive film with a desirable pattern by utilizing the resist layer.

In the method of making a thin-film magnetic head in accordance with this aspect of the present invention, the alignment mark is electrically connected to the multilayer film. Therefore, when the alignment mark is irradiated with a position correcting electron beam in order to correct the drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the multilayer film can be formed into a magnetoresistive film with a desirable pattern.

This aspect of the present invention may further comprise the step of forming an electrically conductive base film in a region to be formed with the alignment mark in the substrate before forming the multilayer film, whereas the multilayer film is formed so as to cover the base film in the step of forming the multilayer film, and a periphery of a part to become the alignment mark in the multilayer film is etched until the base film is exposed in the step of forming the alignment mark so as to form the alignment mark.

Electric charges of the position correcting electron beam irradiating the alignment mark flow into the multilayer film through the base film. On the other hand, the alignment mark contains the multilayer film. If the multilayer film and base film are made of respective materials different from each other when determining the substrate position according to the intensity of reflected electrons at the alignment mark or the like, the intensity of occurring reflected electrons will vary between the alignment mark and its surrounding base film, thus making it easier to determine the position.

Preferably, in this case, the thin-film magnetic head further comprises a first shield layer made of a soft magnetic material between the magnetoresistive film and the substrate, and a second shield film made of a soft magnetic material disposed on a side of the magnetoresistive film opposite from the first shield layer, whereas the first shield layer and the base film made of the same material as that of the first shield layer are formed before the step of forming the multilayer film.

When the first shield layer and the base film are made of the same material, they can be formed together, whereby the manufacturing process can be simplified.

In this aspect of the present invention, the step of forming the alignment mark may be configured such that the alignment mark having an electric conductivity is laminated, on a side of the multilayer film opposite from the substrate, at a position excluding a region to be formed with the magnetoresistive film.

Even when employing a method in which the alignment mark is attached to the multilayer film as such, electric charges of the position correcting electron beam irradiating the alignment mark can be caused to flow into the multilayer film through the base film.

Preferably, in this aspect of the present invention, the alignment mark is irradiated with the position correcting electron beam after an electrically conductive member is brought into contact with the multilayer film.

In this case, electric charges stored in the alignment mark before the irradiation with the position correcting electron beam can be lead to the outside by way of the multilayer film and electrically conductive member. After the electrically conductive member is brought into contact with the multilayer film, the alignment mark may be irradiated with electrons while keeping the contact state, whereby electric charges stored in the alignment mark at the time of irradiation can be led to the outside by way of the multilayer film and electrically conductive member. This prevents the position correcting electron beam from losing its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.

The present invention provides a method of making a magnetoresistive device assembly equipped with a plurality of magnetoresistive devices each having a magnetoresistive film, the method comprising the steps of forming a multilayer film to become the magnetoresistive film on a substrate having an electrically insulating surface; forming an alignment mark, electrically connected to the multilayer film, for correcting a drawing position of a drawing electron beam; coating the multilayer film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; and forming the multilayer film into the magnetoresistive film with a desirable pattern by utilizing the resist layer.

When the alignment mark is irradiated with the position correcting electron beam in the method of making a magnetoresistive device assembly in accordance with this aspect of the present invention, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. Therefore, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Here, the magnetoresistive device assembly encompasses a wafer formed with a plurality of magnetoresistive devices, a bar into which the wafer is divided, and the like.

The method of making a magnetoresistive device assembly in accordance with this aspect of the present invention may comprise the step of forming an electrically conductive base film in a region to be formed with the alignment mark in the substrate before forming the multilayer film, whereas the multilayer film is formed so as to cover the base film in the step of forming the multilayer film, and a periphery of a part to become the alignment mark in the multilayer film is etched until the base film is exposed in the step of forming the alignment mark so as to form the alignment mark.

Electric charges of the position correcting electron beam irradiating the alignment mark flow into the multilayer film through the base film. On the other hand, the alignment mark contains the multilayer film. If the multilayer film and base film are made of respective materials different from each other when determining the substrate position by measuring the intensity of reflected electrons at the alignment mark or the like, the intensity of occurring reflected electrons will vary between the alignment mark and its surrounding base film, thus making it easier to determine the position.

In the method of making a magnetoresistive device assembly in accordance with this aspect of the present invention, the step of forming the alignment mark may be configured such that the alignment mark having an electric conductivity is laminated, on a side of the multilayer film opposite from the substrate, at a position excluding a region to be formed with the magnetoresistive film.

Even when employing a method in which the alignment mark is attached to the multilayer film as such, electric charges of the position correcting electron beam irradiating the alignment mark can be caused to flow into the multilayer film through the base film.

The present invention provides a method of making a magnetic head slider equipped with a thin-film magnetic head having a magnetoresistive film, the method comprising the steps of forming a multilayer film to become the magnetoresistive film on a substrate having an electrically insulating surface; forming an alignment mark, electrically connected to the multilayer film, for correcting a drawing position of a drawing electron beam; coating the multilayer film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; forming the multilayer film into the magnetoresistive film with a desirable pattern by utilizing the resist layer; and cutting the substrate so as to form a magnetic head slider having the magnetoresistive film.

When the alignment mark is irradiated with the position correcting electron beam in the method of making a magnetic head slider in accordance with this aspect of the present invention, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. Therefore, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.

The present invention provides a method of making a head gimbal assembly equipped with a thin-film magnetic head having a magnetoresistive film, the method comprising the steps of forming a multilayer film to become the magnetoresistive film on a substrate having an electrically insulating surface; forming an alignment mark, electrically connected to the multilayer film, for correcting a drawing position of a drawing electron beam; coating the multilayer film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; forming the multilayer film into the magnetoresistive film with a desirable pattern by utilizing the resist layer; cutting the substrate so as to form a magnetic head slider having the magnetoresistive film; and mounting the magnetic head slider to gimbals.

When the alignment mark is irradiated with the position correcting electron beam in the method of making a head gimbal assembly in accordance with this aspect of the present invention, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. Therefore, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. As a consequence, the head gimbal assembly made by way of such a process can form tracks of magnetoresistive films at desirable positions and yield a narrow track width at a high dimensional accuracy, thereby attaining a high magnetic information reproducing performance.

The present invention provides a method of making a hard disk drive equipped with a thin-filmmagnetic head having a magnetoresistive film, the method comprising the steps of forming a multilayer film to become the magnetoresistive film on a substrate having an electrically insulating surface; forming an alignment mark, electrically connected to the multilayer film, for correcting a drawing position of a drawing electron beam; coating the multilayer film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; forming the multilayer film into the magnetoresistive film with a desirable pattern by utilizing the resist layer; cutting the substrate so as to form a magnetic head slider having the magnetoresistive film; mounting the magnetic head slider to gimbals so as to prepare a head gimbal assembly; and assembling the head gimbal assembly such that the magnetic head slider thereof is movable above a hard disk adapted to record a magnetic signal.

When the alignment mark is irradiated with the position correcting electron beam in the method of making a hard disk drive in accordance with this aspect of the present invention, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. Therefore, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. As a consequence, the hard disk drive made by way of such a process can form tracks of magnetoresistive films at desirable positions and yield a narrow track width at a high dimensional accuracy, thereby attaining a high areal density.

The present invention provides a method of making a thin-film magnetic head equipped with a magnetoresistive device having a magnetoresistive film, the method comprising the steps of forming the magnetoresistive film on a substrate having an electrically insulating surface; and forming a process monitoring device having an ohmic value related to an MR height of the magnetoresistive device; the step of forming the process monitoring device including substeps of forming the substrate with a resistance film to become the process monitoring device; forming an alignment mark, electrically connected to the resistance film, for correcting a drawing position of a drawing electron beam; coating the resistance film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; and forming the resistance film into a desirable pattern by utilizing the resist layer so as to form the process monitoring device.

In the method of making a thin-film magnetic head in accordance with this aspect of the present invention, the resistance film, which will later become a process monitoring device, and the alignment mark are electrically connected to each other. Therefore, when the alignment mark is irradiated with a position correcting electron beam in order to correct the drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the resistance film without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the resistance film can be formed into a desirable pattern, whereby a high-performance process monitoring device can be formed.

This aspect of the present invention may comprise the substep of forming an electrically conductive base film in a region to be formed with the alignment mark in the substrate before forming the resistance film, whereas the resistance film is formed so as to cover the base film in the substep of forming the resistance film, and a periphery of a part to become the alignment mark in the resistance film is etched until the base film is exposed in the substep of forming the alignment mark so as to form the alignment mark.

Electric charges of the position correcting electron beam irradiating the alignment mark flow into the resistance film through the base film. On the other hand, the alignment mark contains the resistance film. If the resistance film and base film are made of respective materials different from each other when determining the substrate position by measuring the intensity of reflected electrons at the alignment mark or the like, the intensity of occurring reflected electrons will vary between the alignment mark and its surrounding base film, thus making it easier to determine the position.

In this aspect of the present invention, the substep of forming the alignment mark may be configured such that the alignment mark having an electric conductivity is laminated, on a side of the resistance film opposite from the substrate, at a position excluding a region to be formed with the process monitoring device. Even when employing a method in which the alignment mark is attached to the resistance film as such, electric charges of the position correcting electron beam irradiating the alignment mark can be caused to flow into the resistance film through the base film.

Preferably, in this aspect of the present invention, the alignment mark is irradiated with the position correcting electron beam after an electrically conductive member is brought into contact with the resistance film. In this case, electric charges stored in the alignment mark before the irradiation with the position correcting electron beam can be lead to the outside by way of the resistance film and electrically conductive member. After the electrically conductive member is brought into contact with the resistance film, the alignment mark may be irradiated with electrons while keeping the contact state, whereby electric charges stored in the alignment mark at the time of irradiation can be led to the outside by way of the resistance film and electrically conductive member. This prevents the position correcting electron beam from losing its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.

The present invention provides a method of making a thin-film magnetic head having an induction type recording magnetic transducer, the method comprising the steps of forming a substrate with a first magnetic pole and a second magnetic pole magnetically connected to the first magnetic pole with at least a recording gap layer held therebetween; the step of forming the second magnetic pole including the substeps of forming an electrically conductive magnetic film to become the second magnetic pole; partly removing the magnetic film so as to form an alignment mark for correcting a drawing position of a drawing electron beam; coating the magnetic film with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; and forming the magnetic film into the second magnetic pole with a desirable pattern by utilizing the resist layer.

In the method of making a thin-film magnetic head in accordance with this aspect of the present invention, the electrically conductive magnetic film to become the second magnetic pole is partly removed, so as to form an alignment mark. Therefore, when the alignment mark is irradiated with a position correcting electron beam, electric charges of the electron beam flow into the magnetic film without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the magnetic film can be formed into the second magnetic pole with a desirable pattern.

Preferably, in this aspect of the present invention, the alignment mark is irradiated with the position correcting electron beam after an electrically conductive member is brought into contact with the magnetic film. In this case, electric charges stored in the alignment mark before the irradiation with the position correcting electron beam can be lead to the outside by way of the magnetic film and electrically conductive member. After the electrically conductive member is brought into contact with the magnetic film, the alignment mark may be irradiated with electrons while keeping the contact state, whereby electric charges stored in the alignment mark at the time of irradiation can be led to the outside by way of the magnetic film and electrically conductive member. This prevents the position correcting electron beam from losing its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately.

The present invention provides a method of making a thin-film magnetic head having an induction type recording magnetic transducer, the method comprising the steps of forming a substrate with a first magnetic pole and a second magnetic pole magnetically connected to the first magnetic pole with at least a recording gap layer held therebetween; the step of forming the second magnetic pole including the substeps of forming a plating electrode such that a plurality of forming positions to be formed with the second magnetic pole are electrically connected to each other; forming the plating electrode with an alignment mark for correcting a drawing position of a drawing electron beam; coating the plating electrode with an electron beam resist; irradiating the alignment mark with a position correcting electron beam so as to correct the drawing position; irradiating the electron beam resist with the drawing electron beam at the corrected drawing position so as to form a resist layer with a desirable pattern; and carrying out plating by utilizing the resist layer so as to form the second magnetic pole with a desirable pattern on the plating electrode.

In the method of making a thin-film magnetic head in accordance with this aspect of the present invention, the electrically conductive plating electrode is formed with an alignment mark. Therefore, when the alignment mark is irradiated with a position correcting electron beam, electric charges of the electron beam flow into the plating electrode without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the second magnetic pole with a desirable pattern can be formed on the plating electrode.

The present invention provides a magnetoresistive device assembly equipped with a plurality of magnetoresistive devices each having a magnetoresistive film, the magnetoresistive device assembly comprising a substrate having an electrically insulating surface; the magnetoresistive film formed on the substrate; an alignment mark formed on the substrate, a position of the alignment mark being corrected with an electron beam; and an electrically conductive layer electrically connected to the alignment mark; wherein the electrically conductive layer and the magnetoresistive film are obtained from the same electrically conductive multilayer film.

In the magnetoresistive device assembly in accordance with this aspect of the present invention, the alignment mark has been electrically connected to a multilayer film which is a source of the electrically conductive layer and magnetoresistive film. When the alignment mark is irradiated with a position correcting electron beam in the process of making the assembly for correcting the drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the magnetoresistive film obtained from the multilayer film attains a high positional accuracy.

The present invention provides a magnetoresistive device assembly equipped with a plurality of magnetoresistive devices each having a magnetoresistive film, the magnetoresistive device assembly comprising a substrate having an electrically insulating surface; the magnetoresistive film formed on the substrate; an alignment mark formed on the substrate, a position of the alignment mark being corrected with an electron beam; and an electrically conductive layer electrically connected to the alignment mark; wherein the electrically conductive layer and the magnetoresistive film have the same laminate pattern.

In such a magnetoresistive device assembly, the electrically conductive layer and magnetoresistive film can be obtained from the same multilayer film. In this case, the alignment mark has been electrically connected to the multilayer film that is a source of the electrically conductive layer and magnetoresistive film. When the alignment mark is irradiated with a position correcting electron beam in the process of making the assembly for correcting the drawing position in the subsequent step of electron beam lithography, electric charges of the electron beam flow into the multilayer film without staying in the alignment mark. As a consequence, the position correcting electron beam irradiating the alignment mark does not lose its straightforwardness, whereby the drawing position in electron beam lithography can be corrected accurately. Hence, the magnetoresistive film obtained from the multilayer film attains a high positional accuracy.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention may be more readily described with reference to the accompanying drawings, in which:

FIG. 1 is a perspective view showing an embodiment of hard disk drive made in accordance with the present invention;

FIG. 2 is a perspective view showing a magnetic head slider;

FIG. 3 is an enlarged view of a thin-film magnetic head and its vicinity in FIG. 2;

FIG. 4 is a sectional view of a TMR device and its vicinity;

FIG. 5 is a perspective view showing a substrate formed with a plurality of lower shield layers;

FIG. 6 is a view showing a state where a lower shield layer, a base layer, and a multilayer film are formed on an insulating substrate;

FIG. 7 is a view showing a state where an alignment mark is coated with an electron beam resist after being formed;

FIG. 8 is a view showing a state where an earth pin (electrically conductive member) is inserted into a multilayer film prior to irradiation with a position correcting electron beam;

FIG. 9 is a view showing a state where the alignment mark is irradiated with the position correcting electron beam;

FIG. 10 is a view showing a state where a resist layer is formed by baking after an electron beam resist is irradiated with a drawing electron beam;

FIG. 11 is a view showing a state where liftoff is carried out after forming an insulating layer on a magnetic bias application layer;

FIG. 12 is a view showing another technique of forming an alignment mark;

FIG. 13 is a view showing still another technique of forming an alignment mark;

FIG. 14 is a view showing a state where a resistance film to become a part of a process monitoring device, and a base film are formed on a substrate;

FIG. 15 is a view showing a state where the resistance film is etched, so as to form an alignment mark;

FIG. 16 is a view showing a state where leads are attached to the patterned resistance film, so as to prepare the process monitoring device;

FIG. 17 is a sectional view taken along the line XVII--XVII of FIG. 11 showing a state formed with a recording gap layer, a thin-film coil, and the like;

FIG. 18 is a view illustrating a step of a manufacturing process for preparing an upper magnetic pole in a dry scheme, showing a state where a magnetic film is formed with an alignment mark;

FIG. 19 is a view showing a state where the magnetic film is turned into the upper magnetic pole;

FIG. 20 is a view showing a state where the upper magnetic pole is trimmed, so as to be narrowed;

FIG. 21 is a sectional view showing a state formed with an overcoat layer;

FIG. 22 is a view illustrating a step of a manufacturing process for preparing an upper magnetic pole in a wet scheme, showing a state where a plating electrode is formed on a recording gap layer and then is formed with an alignment mark;

FIG. 23 is an enlarged view of region XXIII in FIG. 22, showing the alignment mark;

FIG. 24A is a perspective view showing a substrate formed with a plurality of thin-film magnetic heads 10, whereas FIG. 24B is a perspective view showing bars obtained by cutting the substrate;

FIG. 25 is a view illustrating a lapping process for MR height adjustment; and

FIG. 26 is a view used for explaining a reason why an electron beam irradiating an alignment mark loses its straightforwardness, which has been found by the inventors in the process of accomplishing the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

In the following, with reference to the accompanying drawings, preferred embodiments of the present invention will be explained in detail. Constituents identical to each other will be referred to with numerals identical to each other without repeating their overlapping explanations.

First, before explaining the manufacturing method of this embodiment, outlines of a thin-film magnetic head, a head gimbal assembly, and a hard disk drive which are obtained by this method will be explained with reference to FIGS. 1 to 4.

FIG. 1 is a view showing a hard disk drive equipped with a thin-film magnetic head obtained by the manufacturing method of this embodiment. This hard disk drive 1 actuates a head gimbal assembly (HGA) 15, and uses a thin-filmmagnetic head 10 for recording and reproducing magnetic information on a recording surface (upper face in FIG. 1) of a hard disk 2 rotating at a high speed. The head gimbal assembly 15 comprises gimbals 12 mounting a slider (magnetic head slider) 11 formed with the thin-film magnetic head 10, and a suspension arm 13 connected thereto, and is rotatable about a shaft 14 by a voice coil motor, for example. As the head gimbal assembly 15 is rotated, the slider 11 moves in a radial direction of the hard disk 2, i.e., in a direction traversing track lines.

FIG. 2 is an enlarged view of the slider 11. In the slider 11, the thin-film magnetic head 10 is formed on a support 11a, made of AlTiC (Al.sub.2O.sub.3.TiC), having a substantially rectangular parallelepiped shape. The front-side face in the drawing is a surface facing the recording surface of the hard disk 2 and is referred to as an air bearing surface (ABS) S. When the hard disk 2 rotates, the airflow caused by the rotation floats the slider 11, thereby separating the air bearing surface S from the recording surface of the hard disk 2. The thin-film magnetic head 10 is provided with recording pads 18a, 18b and reproducing pads 19a, 19b; whereas wires (not depicted), connected to the respective pads, for inputting/outputting electric signals are attached to the suspension arm 13 shown in FIG. 1. Also provided is an overcoat layer 21, indicated by broken lines in the drawing, for protecting the thin-film magnetic head 10. The air bearing surface S may be coated with DLC (Diamond Like Carbon) or the like.

FIG. 3 is an enlarged view schematically showing the thin-film magnetic head 10 formed in the slider 11. For explaining its outlines, the thin-film magnetic head 10 is shown in this drawing in a partly broken state, while omitting layers which will not be mentioned. On the support 11a, an undercoat layer 11b made of an electrically insulating material such as alumina (Al.sub.2O.sub.3) is formed, on which the thin-film magnetic head 10 is formed.

The thin-film magnetic head 10 is a combination thin-film magnetic head in which a reproducing head section 30 having a TMR device as a magnetoresistive device and a recording head section 60 as an induction type magnetic transducer are combined together. The TMR device employs a TMR film utilizing a tunnel effect and yielding a magnetoresistance change ratio higher than that of GMR films.

The reproducing head section 30 mainly comprises a lower shield layer (first shield layer) 32 also acting as a lower electrode; a lower gap layer 34 formed from a nonmagnetic, electrically conductive material; a TMR device 40; insulating layers 36 disposed on both sides thereof; and an upper shield layer (second shield layer) 38, formed on the TMR device 40, also acting as an upper electrode. The lower gap layer 34 is used for adjusting the lead gap corresponding to the recording density of a recording medium to a desirable value. The lower shield layer 32 and upper shield layer 38 function to prevent the TMR device from sensing unnecessary external magnetic fields. The TMR device 40 has a TMR film 42 and magnetic bias application layers 43 which are disposed on both sides thereof and made of a hard magnet or the like, for example. Though not depicted, the lower shield layer 32 (lower electrode) and the upper shield layer 38 (upper electrode) are electrically connected to the reproducing pads 19a and 19b (see FIG. 2), respectively. In the specification, words "upper" and "lower" used as in the shield layers refer to the sides closer to and further from the support 11a, respectively.

FIG. 4 is a sectional view of the TMR device 40 and its vicinity at a location slightly inside of the air bearing surface S in the vertical direction. The TMR film 42 of the TMR device 40 comprises a free layer 44 containing a ferromagnetic material, whose magnetization direction is variable according to external magnetic fields; a tunnel barrier layer 45 which is a nonmagnetic, insulating, thin film through which electrons can pass while maintaining their spins due to a tunnel effect; a pinned layer 46 containing a ferromagnetic material, whose magnetization direction is held constant without being affected by external magnetic fields; and a pinning layer 47 for fixing the magnetization direction (depth direction of the drawing sheet) of the pinned layer 46. Preferably, a cap layer made of Ta, NiCr, or the like, for example, for preventing the TMR film from oxidizing is formed on the pinning layer 47. The magnetic bias application layers 43 apply a bias magnetic field to the free layer 44 of the TMR film 42 in horizontal directions in FIG. 4.

In the following manner, such are producing head section 30 reproduces magnetic information recorded in the hard disk 2. Namely, when a voltage is applied between the reproducing pads 19a, 19b (see FIG. 2), electrons flow from the pinned layer 46 into the free layer 44 through the tunnel barrier layer 45, which is an insulating layer. As mentioned above, the magnetization direction of the free layer 44 is changeable by external magnetization, i.e., magnetization of the hard disk 2. The ohmic value becomes lower when the respective magnetization directions of the pinned layer 46 and free layer 44 are parallel to each other, and becomes higher when they are not parallel. Utilizing these phenomena, the magnetic information recorded in the hard disk 2 is read out according to the relative angle between the respective magnetization directions of the free layer 44 and pinned layer 46.

Referring to FIG. 3 again, the recording head section 60 of the thin-film magnetic head 10 will be explained. The recording head section 60 is disposed on the reproducing head section 30 by way of an insulating layer 39, and acts as an induction type magnetic transducer. The insulating layer 39 is not always necessary. The recording head section 60 mainly comprises a lower magnetic layer 61; a lower magnetic pole (first magnetic pole) 61a formed by partly trimming the lower magnetic layer 61; a recording gap layer 62 made of an insulating material; an upper magnetic pole (second magnetic pole) 64a formed on the recording gap layer 62 and magnetically connected to the lower magnetic pole 61a (lower magnetic layer 61) by way of an upper magnetic layer 64; and a plurality of thin-film coils 66. Though the processes of preparing the upper magnetic pole 64a and the upper magnetic layer 64 are separated from each other in this example, they may be made at once by the same process. The recording gap layer 62 is formed with an opening 62a at the center part of the thin-film coils 66, whereby the upper magnetic pole 64a and the lower magnetic pole 61a are magnetically connected to each other through the opening 62a. The recording pads 18a, 18b (see FIG. 2) are electrically connected to the thin-film coils 66.

In the following manner, such a recording head section 60 records information onto the hard disk 2. Namely, when a recording current is caused to flow through the thin-film coils 66 by way of the recording pads 18a, 18b, a magnetic field occurs between the lower magnetic pole 61a and upper magnetic pole 64a. Then, a magnetic flux occurring near the recording gap layer 62 magnetizes the hard disk 2, thereby recording the information.

The foregoing are outlines of the thin-film magnetic head, head gimbal assembly, and hard disk drive obtained by the manufacturing method of this embodiment. With reference to FIGS. 5 to 25, the manufacturing method of this embodiment will now be explained.

The making of the thin-film magnetic head 10 is carried out by a procedure in which the part corresponding to the reproducing head section 30 is prepared and then the part corresponding to the recording head section 60 is prepared. First, as shown in FIG. 5, an undercoat layer 11b made of an insulating material such as alumina (Al.sub.2O.sub.3), for example, is formed by a thickness of about 1 .mu.m to about 10 .mu.m by sputtering on a wafer-like substrate 30 made of AlTiC (Al.sub.2O.sub.3.TiC), for example, so as to form an electrically insulating substrate. The substrate 30 becomes a support 11a for the slider 11 in a later step. Though only the surface of the substrate requires an electrically insulating property, a substrate made of an insulating material as a whole may be used as well. Subsequently, on the undercoat layer 11b, a lower shield layer 32 made of a soft magnetic material such as NiFe (Permalloy) is formed by a thickness of about 1 .mu.m to about 3 .mu.m by plating, for example. Also, as shown in the same drawing, the lower shield layer 32 is formed at each of matrix-like forming positions where TMR devices 40 will be formed later.

By the same material (e.g., NiFe) as that of the lower shield layer 32, an electrically conductive base film 81 is formed in a region to be formed with an alignment mark which will be explained later. As with the lower shield layer 32, the base film 81 can be formed by plating or the like. Then, the part other than those formed with the base film 81 and lower shield layer 32 is buried under an insulating layer 11c such as alumina (Al.sub.2O.sub.3) until its surface level is on a par with that of the lower shield layer 32 (see FIG. 6). Regions 52a indicated by broken lines in FIG. 5 illustrate positions of process monitoring devices which will be provided later. A process monitoring device is formed for each or a predetermined number of reproducing heads. The lower shield layer 32 is formed with spaces for providing the process monitoring devices.

Referring to FIG. 6, the next step will be explained. FIG. 6 is a sectional view taken along the line VI-VI in FIG. 5. A lower gap layer 34 is formed by a thickness of about 1 nm to about 70 nm on the lower shield layer 32, for example, by sputtering. Examples of materials forming the lower gap layer 34 include Cu, Al, Au, Ta, and NiCr.

Subsequently, a multilayer film 42a is formed on substantially the whole surface of the substrate 30 so as to cover the lower gap layer 34 and base film 81. The multilayer film 42a will later be patterned into a TMR film 42. Specifically, a free layer 44, a tunnel barrier layer 45, a pinned layer 46, and a pinning layer 47 are laminated in this order, for example, by sputtering. Preferably, a cap layer for preventing the TMR film 42 from oxidizing is formed on the pinning layer 47. The free layer 44 has a thickness of about 1 nm to about 10 nm and can be formed from a ferromagnetic material such as NiFe or CoFe. The tunnel barrier layer 45 has a thickness of about 0.5 nm to about 2 nm and can be formed from an insulating material such as Al.sub.2O.sub.3, NiO, MgO, or TiO.sub.2, for example. An example of techniques for forming the tunnel barrier layer 45 from Al.sub.2O.sub.3 comprises the steps of forming a film of Al on the free layer 44 and then oxidizing thus formed film. The pinned layer 46 has a thickness of about 1 nm to about 10 nm and can be formed from a ferromagnetic material such as Fe, Co, Ni, or CoFe. The pinning layer 47 has a thickness of about 5 nm to about 30 nm and can be formed from an anti ferromagnetic material such as PtMn, for example, which can fix the magnetization direction of the pinned layer 46.

Next, as shown in FIG. 7, surroundings of the part to become an alignment mark in the multilayer film 42a are etched (for which ion milling, RIE, and the like are usable) until the base film 81 is exposed, so as to form the alignment mark 82. The form of alignment mark 82 is variable without being restricted to the depicted one. In this drawing, the individual layers of the multilayer film 42a are not depicted, whereas the cross section is not completely hatched (thus yielding a schematic view). The alignment mark 82 is formed from the material of the multilayer film 42a, and thus has an electric conductivity. The alignment mark 82 is formed such that the contact part between the base film 81 and multilayer film 42a is left. As a consequence, the alignment mark 82 is electrically connected to the multilayer film 42a by way of the base film 81. After forming such an alignment mark 82, an electron beam resist 49 is applied onto the multilayer film 42a (on the side opposite from the substrate 30) so as to cover the whole surface of the substrate 30. Here, the electron beam resist 49 is of negative type whose part irradiated with an electron beam will remain as a resist layer. Though this embodiment uses a chemically amplified resist, other kinds of electron beam resists can be employed as well.

Before irradiating the alignment mark with a position correcting electron beam, this embodiment takes the following step. Namely, as shown in FIG. 8, the front end part of an electrically conductive earth pin (electrically conductive member) 50 having the grounded potential, made of Cu, for example, provided in an electron beam drawing apparatus is inserted into the multilayer film 42a of the substrate 30 supported by a susceptor 51. In this embodiment, the earth pin 50 is inserted near the outer periphery of the substrate 30. When the earth pin 50 is inserted into the multilayer film 42a as such, electric charges stored in the multilayer film 42a and alignment mark 82 in various steps so far flow out through the earth pin 50.

Subsequently, for correcting a drawing position in a later step, the alignment mark 82 of the substrate 30 is initially scanned with the position correcting electron beam as shown in FIG. 9, and the intensity of reflected electrons occurring at this time is measured. After the position of the alignment mark 82 is detected according to the intensity of reflected electrons, the position of an optical system irradiating a drawing electron beam in the subsequent step or the position of a stage supporting the substrate is corrected according to thus detected position.

In this embodiment, the alignment mark 82 is electrically connected to the multilayer film 42a by way of the base film 81. Therefore, when the alignment mark 82 is irradiated with the position correcting electron beam as schematically indicated by an arrow in FIG. 9, electric charges of the electron beam flow into the multilayer film 42a without staying in the alignment mark 82. As a consequence, the position correcting electron beam irradiating the alignment mark 82 does not lose its straightforwardness, whereby drawing positions in electron beam lithography can be corrected accurately. Hence, the multilayer film 42a can be formed into the TMR film 42 with a desirable pattern in the subsequent step.

Also, since the earth pin 50 is inserted in the multilayer film 42a as shown in FIG. 8, electric charges stored in the alignment mark 82 at the time of irradiation with the position correcting electron beam move from the multilayer film 42a to the outside through the earth pin 50, whereby electric charges can more reliably be prevented from causing charge-up in the alignment mark 82. Here, the electrically conductive member for moving electric charges of the TMR film 42 to the outside can be changed into various forms without being restricted to the needle-like earth pin 50. For example, it is not always required to be pointed, although a pointed electrically conductive member is preferred for making it easier to be inserted into the multilayer film 42a. Also, electric charges can be moved to the outside of the multilayer film 42a if the earth pin 50 is brought into contact with the surface of the multilayer film 42a even without inserting it to the inside.

In this embodiment, the alignment mark 82 is formed on the base film 81, whereas the base film 81 is exposed in the periphery of the alignment mark 82. The baser film 81 is made of the same material (e.g., NiFe) as that of the lower shield layer 32. The alignment mark 82 is constituted by the same material as that of the multilayer film 42a. The uppermost pinned layer is made of PtMn, which is an antiferromagnetic material. In the case where the alignment mark 82 and the base film 81 are formed from respective materials different from each other as such, the intensity of reflected electrons occurring in the alignment mark 82 differs from that of reflected electrons occurring in its surrounding base film 81 when the alignment mark 82 and its vicinity are scanned with the position correcting electron beam for positional correction, whereby positional measurement becomes easier. The base film 81 may also be formed so as to be laminated on the insulating layer 11c instead of being surrounded thereby. Even in the latter case, electric charges of the position correcting electron beam irradiating the alignment mark 82 flow into the multilayer film 42a through the base film 81.

Since the base film 81 is formed from the same material as that of the lower shield layer 82, they can be formed together by plating, for example, whereby the manufacturing process can be simplified in this embodiment.

After the correction of drawing position of drawing electron beam is completed, a desirable area on the lower gap layer 34 in the electron beam resist 49 is irradiated with a drawing electron beam from an electron gun (not depicted), so as to form a latent image pattern 48a (region hatched with broken lines in the drawing). Here, the drawing electron beam may be either identical to or different from the position correcting electron beam outputted from the electron gun used for irradiating the alignment mark. Thereafter, post-exposure baking is carried out, and then a developing solution is used, so as to attain a resist layer 48 with a desirable pattern.

FIG. 10 is a view showing the laminate structure after the development. As depicted, the resist layer 48 is formed with undercuts 48c on both sides of its lower part. Forming such undercuts 48c facilitates liftoff which will be performed later. The undercuts 48c can be formed, for example, by coating the multilayer film 42a with a layer of polymethylglutarimide (PMGI) having a low molecular weight and then applying an electron beam resist onto this layer as disclosed in Japanese Patent Publication No. HEI 7-6058.

Referring to FIG. 11, the next step will be explained. First, using the resist layer 48 as a mask, the multilayer film 42a is selectively etched by ion milling or the like, for example, so as to form a TMR film 42 with a desirable minute pattern. Thereafter, a pair of magnetic bias application layers 43 are formed on both sides of the TMR film 42 by sputtering, for example, so as to yield a TMR device 40. The magnetic bias application layers 43 are formed from a high-coercivity material such as CoPt, for example. Then, an insulating layer 36 made of Al.sub.2O.sub.3 or the like is formed by sputtering, for example, so as to cover the lower shield layer 32, lower gap layer 34, and magnetic bias application layers 43. In FIGS. 3 and 4, the insulating layers 11c and 36 are collectively referred to as the insulating layer 36 since they are formed from the same material (alumina).

Thereafter, liftoff is carried out with a release liquid, so as to remove the resist layer 48 together with the materials laminated thereon. An alternative process may comprise the steps of forming a resist layer having a desirable pattern by using a positive type electron beam resist while leaving the vicinity of the part to be formed with the TMR film 42; forming a metal oxide film, for example, by sputtering or the like on the resist layer and the part not covered with the resist layer; and then etching the multilayer film 42a while using the metal oxide film with the desirable pattern obtained by liftoff as a mask. Such a process can also form the TMR film 42 by using the resist layer. Further, an upper shield layer 38 made of a soft magnetic material is formed by plating, for example, so as to cover the TMR film 42 and insulating layer 36. An example